PETG-413 is a glass fiber-reinforced PETG granule (30% glass fiber by weight) designed specifically for large-area additive manufacturing (BAAM). It offers excellent printability, warpage resistance, and weatherability. With superior strength, durability, and resistance to heat, pressure, and chemicals, PETG-413 is an ideal material for both 3D printing and injection molding, suitable for a wide range of applications.

 

FGF-高分子颗粒料-ABS-108FR-

Reinforced PETG for Large Scale Manufacturing

PETG-413 offers strength, durability, and excellent printability.
Easy Processing
High Toughness
High Cost-Effectiveness
Excellent Chemical Resistance
  • FGF-高分子颗粒料-ABS-108FR-
<
>

Technical Datasheet

Physical Properties

Property Test Method Value
Density (g/cm3 , 21.5 °C) ASTM D792(1S0 1183,GB/T 1033) 1.39
Distortion temperature (°C) DSC,10 C/min 81
Glasstransition temperature (°C) ISO75 18MPa 77
0.45MPa 82

 

Mechanical Properties

Property Test Method Value
Flexural Modulus(MPa)(X-Y) Modified ASTM D790(IS0 178,GB/T 9341) 6094+1344
Flexural Strength(MPa)(X-Y) Modified ASTM D790(IS0 178,GB/T 9341) 128.1 + 7.8
Impact strength(kJ/m3)(X-Y) Modified ASTM D256(IS0 179,GB/T 1043) 21.3 + 0.92
Flexural Modulus(MPa)(Z) Modified ASTM D790(IS0 178,GB/T 9341) 2701+ 366
Flexural Strength(MPa)(Z) Modified ASTM D790(IS0 178,GB/T 9341) 46.8 +3.3
Impact strength(kJ/m3) (Z) Modified ASTM D256(IS0 179, GB/T 1043) 5.2 + 1.3

 

 

 

 