PLA granule is a new bio-based and biodegradable material made of starch
from plant resources (such as corn). It has good biodegradability and is recognized as
an environmentally friendly material. Suitable for indoor decorative furniture and
other scenes. The material is bubble-free with a glossy finish and a particle diameter of approximately 3mm.

 

Snipaste_2024-12-12_17-37-10

P716-ABS Eco-Friendly Pellets

P716-ABS granules are eco-friendly, biodegradable, glossy, and ideal for indoor use.
High Gloss
High Rigidity
Medium Impact
General Grade
  • Snipaste_2024-12-12_17-37-10
<
>

Technical Datasheet

 

Physical Property Testing Standards Data Unit
Melt index 220°C 10kg ASTM D1238 197 g/10min
Melt index 220°C 10kg ISO 1133 197 g/10min
Melt index 200°C 5kg ASTM D1238 65 g/10min
Melt index 200°C 5kg ISO 1133 65 g/10min

 

Hardness Testing Standards Data Unit
Rockwell hardness R scale 23°C ASTM D785 84 /
Rockwell hardness R scale 23°C ISO 2039 84 /

 

Mechanical Character Testing Standards Data Unit
Tensile strength ASTM D638 50.5 MPa
Young’s Modulus ASTM D638 4780 MPa
Elongation at break ASTM D638 9.6 %
Flexural Strength ASTM D790 76 MPa
Flexural Modulus ASTM D790 24800 MPa
Flexural Modulus ASTM D256 48 J/m

 

Hot Property Testing Standards Data Unit
Heat Deflection(HDT) ASTM D648 54.5 °C
Glass Transition(Tg) ASTM D7426 58.8 °C
Melting Point ASTM D7426 162.6 °C
Decomposition Temp@5% ASTM E2402 ≥374 °C
Vicat Softening Tem ASTM D1525 54 °C
Mold Shrinkag ASTM D955 0.1-0.3 %

 

Others Testing Standards Data Unit
Melt Flow Rate ASTM D1238 10 g/10min
Density ASTM D792 1.3 g/cm3
Volume Resistivity ASTM D257 2.90E+15 ohm-cm
Dielectric Constant ASTM D150 1.51 /
Flammability UL94 HB Class

 

 